Drug core aluminum wire advantage

First, the production efficiency is different

Compared with solid wire, flux cored wire adopts continuous welding mode, less welding spatter and good weld forming, so it reduces the time of cleaning spatter and repairing weld surface, so the production efficiency is higher than solid wire.Two, the use of different costsFlux cored wire itself is very expensive compared to solid wire. But for large enterprises, after using flux cored wire, the production cycle is shortened and the weld quality is easy to guarantee, so the comprehensive benefits are very high.

Use different

1, flux cored wire: flux cored wire is mainly used for flat welding and fillet welding, used for welding construction machinery, heavy machinery, steel frame, bridge, etc.2, solid wire: solid wire is widely used in welding work, is used as a filler metal or at the same time as a conductive metal wire welding material. In gas welding and TUNGSTEN gas shielded arc welding, welding wire is widely used as filler metal. In submerged arc welding, electroslag welding and other gas shielded arc welding, welding wire is both filler metal and conductive electrode.

Four, the adaptability of steel is different

1, flux cored wire: because flux cored wire is generally through flux cored transition alloy elements, so you can easily adjust the alloy composition from the formula like manual electrode, to meet the requirements of the welded steel.

2, solid wire: solid wire every adjustment of the alloy composition, it is necessary to re smelting, the process is more difficult to control, so it is difficult to meet the requirements of less and more varieties. And some alloy steel solid core wire drawing performance is poor, it is difficult to pull into the required wire.

Reference source: Baidu Encyclopedia - flux cored wire

Product specification: Material: aluminum silicon, color: silver, working temperature: 420°

Diameter: 2mm/0.08", 1.6mm/0.06"

Length: 500 mm /19.7 in

Low temperature aluminum aluminum welding wire can weld aluminum, aluminum alloy, aluminum magnesium alloy, and other white metal.

It is suitable for the primary welding operator to weld in all aspects, only the heating device efficiency is enough, the weld strength after welding is higher than the hardness of the base metal, and you can know the welding operation.

Low temperature aluminum aluminum welding wire instructions:

Step 1: through physical cleaning, polishing the surface, cleaning the welding surface oil ester and steel brush or copper brush to remove electric coating, rust, paint, oil, oxide and other coating.

Step 2: heating of the surface of the parent metal welds (do not directly burn electrode), until the temperature reached the welding wire is the working temperature of 550 degrees, electrode to reliable close together so that you can rely on heating electrode parent metal hot fu guide melting weld, and only when the parent metal surface temperature enough wire to flow and well ZhanMao fine permeate into gold.

The third step: when repairing thin aluminum parts, as long as the aluminum base material is heated to the appropriate working temperature, and then friction melting welding wire back and forth to form a weld, only with gold high brush melting welding wire fill in the welding place to form a weld.

PS. Pay attention to details

1, the surface of the base material must be cleaned, that is, clean welding. (Clean refers to the removal of electroplating, rust, paint, oil, oxide, etc.)

2, the temperature of the base material must reach 550℃, including the temperature of the base material in the process of welding should also be maintained at about 550℃