Use in aluminum alloy, please use a good heating efficiency flamethrower

Aluminum flux cored electrode use: applied to aluminum parts (not dissimilar phase), welding without additional flux,

Direct welding operation, no need to add welding powder, good fluidity of the solder joint firm

Material: Aluminum silicon, color: silver, working temperature: 550°

Diameter: 2mm/0.08", 1.6mm/0.06"

Length: 500 mm /19.7 in

Low temperature aluminum aluminum welding wire can weld aluminum, aluminum alloy, aluminum magnesium alloy, and other white metals.

Suitable for primary welding operators all-directional welding, only the heating device efficiency is enough, welding weld strength after welding is generally higher than the hardness of the base metal, welding operation can be understood.

Instructions for use of low temperature aluminum welding wire:

Step 1: BY PHYSICALLY CLEANING, POLISHING THE SURFACE, CLEANING THE OIL ESTER ON THE WELDING SURFACE AND USING STEEL OR COPPER BRUSH TO REMOVE ELECTROPLATING, RUST, PAINT, GREASE, OXIDE, ETC.

Step 2: heating of the surface of the parent metal welds (do not directly burn electrode), until the temperature reached the welding wire is the working temperature of 550 degrees, electrode to reliable close together so that you can rely on heating electrode parent metal hot fu guide melting weld, and only when the parent metal surface temperature enough wire to flow and well ZhanMao fine permeate into gold.

The third step: when repairing the thin aluminum parts, as long as the aluminum base metal is heated to the appropriate working temperature, and then the welding wire is rubbed back and forth to form a weld, and only the welding wire is filled with gold high brush to form a weld.

PS. Operation attention to detail

1, the surface of the base material must be cleaned, that is, welding (clean refers to the removal of electroplating, corrosion, paint, oil, oxide, etc.)

2. The temperature of the base metal must reach 550℃, including the temperature of the base metal in the process of welding should also be maintained at about 550℃