Product specifications

Material: Aluminum

Color: silver

Working temperature: 420°

Diameter: 2mm/0.08", 1.6mm/0.06"

Length: 500 mm/19.7 inches

Commodity description: Low-temperature aluminum aluminum welding wire can weld aluminum, aluminum alloy, aluminum-magnesium alloy, and other white metals.

It is suitable for all-round welding by primary welding operators, only the heating device is efficient enough, and the weld strength after welding is generally higher than the hardness of the base metal, and it is enough to know the welding operation.

Instructions for use of low temperature aluminum aluminum welding wire:

The first step: through physical cleaning, polishing the surface, cleaning the grease on the surface of the weld, and using a steel brush or copper brush to remove the plating layer, rust, paint, oil, oxide and other coatings.

Step 2: Heat the surface of the base metal at the welding point (do not burn the electrode directly) until the temperature reaches 550 degrees, the working temperature of the welding wire, then the welding rod can be heated close together so that the welding rod can be melted by the heat conduction of the base material to form a weld. , And only when the surface temperature of the base metal is sufficient, the welding wire can flow and penetrate to the Jinzhan capillary well.

The third step: When repairing thin aluminum parts, just heat the aluminum base material to a suitable working temperature, and then use the welding wire to friction and melt back and forth to form a weld. Only use the gold high brush to fill the weld with the molten wire to form the weld. .

PS. Pay attention to details of operation

1. The surface of the base metal must be cleaned up, that is, cleaned and welded. (Cleaning up refers to removing the electroplating layer, rust, paint, oil, oxide, etc.)

2. The temperature of the base metal must reach 550℃, including the temperature of the base metal during the welding process should be kept at about 550℃